Question:
In the iron-carbon equilibrium phase diagram, the temperature and composition of the eutectoid point are 727 °C and 0.77 weight % carbon, respectively. If a steel specimen with 1.2 weight % carbon is cooled from 1000 °C to the room temperature, then the fraction of pro-eutectoid cementite phase in the steel is _____ . (Rounded off to 2 decimal places)
In the iron-carbon equilibrium phase diagram, the temperature and composition of the eutectoid point are 727 °C and 0.77 weight % carbon, respectively. If a steel specimen with 1.2 weight % carbon is cooled from 1000 °C to the room temperature, then the fraction of pro-eutectoid cementite phase in the steel is _____ . (Rounded off to 2 decimal places)
Updated On: Jul 12, 2024
- 0.07
- 0.93
- 0.18
- 0.12
Hide Solution
Verified By Collegedunia
The Correct Option is A
Solution and Explanation
The correct option is (A): 0.07
Was this answer helpful?
0
0
Top Questions on Phase diagrams
- Fluidity of a molten alloy during sand casting depends on its solidification range. The phase diagram of a hypothetical binary alloy of components A and B is shown in the figure with its eutectic composition and temperature. All the lines in this phase diagram, including the solidus and liquidus lines, are straight lines. If this binary alloy with 15 weight % of B is poured into a mould at a pouring temperature of 800\,$^\circ$C, then the solidification range is ________________.
- A shaft of diameter \(25^{-0.04}_{-0.07}\) mm is assembled in a hole of diameter \(25^{+0.02}_{+0.00}\) mm. Match the allowance and limit parameter in Column I with its corresponding quantitative value in Column II for this shaft–hole assembly.
- In the vicinity of the triple point, the equation of liquid-vapor boundary in the \(P - T\) phase diagram for ammonia is \( \ln P = 24.38 - \frac{3063}{T} \), where \(P\) is pressure (in Pa) and \(T\) is temperature (in K). Similarly, the solid-vapor boundary is given by \( \ln P = 27.92 - \frac{3754}{T} \). The temperature at the triple point is ________ K (round off to one decimal place).
Questions Asked in GATE PI exam
A through hole of 10 mm diameter is to be drilled in a mild steel plate of 30 mm thickness. The selected spindle speed and feed for drilling hole are 600 revolutions per minute (RPM) and 0.3 mm/rev, respectively. Take initial approach and breakthrough distances as 3 mm each. The total time (in minute) for drilling one hole is ______. (Rounded off to two decimal places)
- GATE PI - 2026
- Machining Processes and Machine Tools
In a cold rolling process without front and back tensions, the required minimum coefficient of friction is 0.04. Assume large rolls. If the draft is doubled and roll diameters are halved, then the required minimum coefficient of friction is ___________. (Rounded off to two decimal places)
- GATE PI - 2026
- Machining Processes and Machine Tools
- Which one of the following casting defects is caused due to the supply of the molten metal through two gates?
- GATE PI - 2026
- Machining Processes and Machine Tools
- The relationship between the hoop stress \(\sigma_1\) and the longitudinal stress \(\sigma_2\) of a closed cylindrical thin-walled pressure vessel is
- GATE PI - 2026
- Machining Processes and Machine Tools
- Three principal stresses at a point in a material are 300 MPa, 250 MPa, and 100 MPa. If the yielding just starts at that point, the yield strength (in MPa) of the material as per Tresca criterion is ............
Answer: The yield strength lies between 199 to 201 MPa.- GATE PI - 2025
- Industrial and Production
View More Questions